CuZn40Mn1Pb1 (CW720R)
| Darajasi: | CuZn40Mn1Pb1 |
| Raqam: | CW720R |
| Tasnifi: | Murakkab mis-sink qotishmasi |
| Zichlik | 8,3 g/sm³ |
| Standart: | EN 12164: 1998 Mis va mis qotishmalari. Bepul ishlov berish uchun novda EN 12166: 1998 Mis va mis qotishmalari. Umumiy maqsadlar uchun sim EN 12167: 1998 Mis va mis qotishmalari. Umumiy maqsadlar uchun profillar va to'rtburchaklar bar EN 12168: 1998 Mis va mis qotishmalari. Bepul ishlov berish uchun ichi bo'sh novda EN 12165: 1998 Mis va mis qotishmalari. Buzilgan va ishlov berilmagan zarb zahiralari EN 12420: 1999 Mis va mis qotishmalari. Soxta buyumlar |
| Ekvivalent baholar: | Bu yerga boring |
Kimyoviy tarkibi % sinf CuZn40Mn1Pb1 (CW720R)
| Fe | Si | Mn | Ni | Al | Cu | Pb | Sn | Boshqalar | - |
| maksimal 0.3 | maksimal 0.1 | 0.5 - 1.5 | maksimal 0.6 | maksimal 0.2 | 57 - 59 | 1 - 2 | maksimal 0.3 | jami 0.3 | Zn - qoldiq |
CuZn40Mn1Pb1 (CW720R) sinfining mexanik xususiyatlari
| Rm- Kuchlanish kuchi (MPa) (R390) | 390 |
| Rm- Kuchlanish kuchi (MPa) (R440) | 440 |
| Rp0.20.2% chidamlilik (MPa) (R390) | 200 |
| Rp0.20.2% chidamlilik (MPa) (R440) | 250 |
| A- min. sinish cho'zilishi (%) (R390) | 20 |
| A- min. sinish cho'zilishi (%) (R440) | 18 |
| Brinell qattiqligi (HB): (R390) | 110 |
| Brinell qattiqligi (HB): (R440) | 120 |
CuZn40Mn1Pb1 (CW720R) sinfining ekvivalent navlari
Ogohlantirish! Faqat ma'lumot uchun
| EI UZ |
Germaniya DIN, WNr |
||
| CuZn40Mn1Pb1 |
|
Kasting jarayoni
| GS | Qum quyish |
| GM | Doimiy qolib quyish |
| GZ | Santrifüj quyish |
| GC | Uzluksiz quyish |
| GP | Bosimli quyma |
Moddiy sharoitlar
| R | Majburiy kuchlanish va cho'zilish talablari bo'lgan mahsulot uchun valentlik kuchi talabining minimal qiymati bilan belgilanadigan moddiy holat |
| H | Majburiy qattiqlik talablari bo'lgan mahsulot uchun qattiqlik talabining minimal qiymati bilan belgilanadigan moddiy holat |
Mexanik xususiyatlar
| ReH | Minimal rentabellik kuchi / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Kuchlanish kuchi / Zugfestigkeit / Qarshilik a la tortishish |
| A | Minimal cho'zilish / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Notch zarbasi testi / Kerbschlagbiegeversuch / Essai de fleksiyon par choc |
|
CuZn40Mn1Pb1 (CW720R) murakkab mis-sink qotishmasi |