CuSn11P-C ( CC481K )
| Darajasi: |
CuSn11P-C |
| Raqam: |
CC481K |
| Tasnifi: |
Mis{0}}qalay qotishmasi |
| Standart: |
EN 1982: 2008 Mis va mis qotishmalari. Quyma va quyma |
| Ekvivalent baholar: |
Bu yerga bor |
Kimyoviy tarkibi % CuSn11P-C ( CC481K )
| Quyma shaklidagi materialni aniqlash uchun belgiga -C qo'shimchasi qo'shiladi |
| Fe |
Si |
Mn |
Ni |
P |
S |
Al |
Cu |
Pb |
Zn |
Sb |
Sn |
| maksimal 0,1 |
maksimal 0,01 |
maksimal 0,05 |
maksimal 0,1 |
0.5 - 1 |
maksimal 0,05 |
maksimal 0,01 |
87 - 89.5 |
maksimal 0,25 |
maksimal 0,05 |
maksimal 0,05 |
10 - 11.5 |
CuSn11P-C ( CC481K ) sinfining mexanik xususiyatlari
| Rm- Uzilish kuchi (MPa) (GS) |
250 |
| Rm- Uzilish kuchi (MPa) (GM) |
310 |
| Rm- Uzilish kuchi (MPa) (GC) |
350 |
| Rm- Chiqish kuchi (MPa) (GZ) |
330 |
| Rp0.20,2% chidamlilik (MPa) (GS) |
130 |
| Rp0.20,2% chidamlilik (MPa) (GM) |
170 |
| Rp0.20,2% chidamlilik (MPa) (GC) |
170 |
| Rp0.20,2% chidamlilik (MPa) (GZ) |
170 |
| A- min. sinish cho'zilishi (%) (GS) |
5 |
| A- min. sinish cho'zilishi (%) (GM) |
2 |
| A- min. sinish cho'zilishi (%) (GC) |
5 |
| A- min. sinish cho'zilishi (%) (GZ) |
4 |
| Brinell qattiqligi (HBW): (GS) |
60 |
| Brinell qattiqligi (HBW): (GM) yoki (GC) yoki (GZ) |
85 |
CuSn11P-C ( CC481K ) sinfining ekvivalent baholari
Ogohlantirish! Faqat ma'lumot uchun
EI
UZ |
Germaniya
DIN, WNr |
Angliya
BS |
Polsha
PN |
Chexiya
CSN |
Inter
ISO |
| CuSn11P-C |
|
|
|
|
|
Kasting jarayoni
| GS |
Qum quyish |
| GM |
Doimiy qoliplarni quyish |
| GZ |
Santrifüj quyish |
| GC |
Uzluksiz quyish |
| GP |
Bosimli quyma |
Moddiy sharoitlar
| R |
Majburiy kuchlanish va cho'zilish talablari bo'lgan mahsulot uchun valentlik kuchi talabining minimal qiymati bilan belgilanadigan moddiy holat |
| H |
Majburiy qattiqlik talablari bo'lgan mahsulot uchun qattiqlik talabining minimal qiymati bilan belgilanadigan moddiy holat |
Mexanik xususiyatlar
| ReH |
Minimal rentabellik kuchi / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm |
Kuchlanish kuchi / Zugfestigkeit / Qarshilik a la tortishish |
| A |
Minimal cho'zilish / Mindestwert der Bruchdehnung / Allongement minimal |
| J |
Notch zarbasi testi / Kerbschlagbiegeversuch / Essai de fleksiyon par choc |
|
CuSn11P-C ( CC481K ) Mis-qalay qotishmasi
Kimyoviy tarkibi. CuSn11P-C ( CC481K ) ekvivalentlari.
Standartlar.1 Mexanik xususiyatlar. Qattiqlik
|